{"product_id":"ieej-mag11117","title":"Fe－Si合金アトマイズ粉末を用いた圧粉磁心の直流重畳特性に及ぼす粉末粒径の影響とそのモデル化","description":"\u003cp\u003e\u003cstrong\u003eカテゴリ: \u003c\/strong\u003e研究会(論文単位)\u003c\/p\u003e\u003cp\u003e\u003cstrong\u003e論文No: \u003c\/strong\u003eMAG11117\u003c\/p\u003e\u003cp\u003e\u003cstrong\u003eグループ名: \u003c\/strong\u003e【A】基礎・材料・共通部門 マグネティックス研究会\u003c\/p\u003e\u003cp\u003e\u003cstrong\u003e発行日: \u003c\/strong\u003e2011\/11\/29\u003c\/p\u003e\u003cp\u003e\u003cstrong\u003eタイトル(英語): \u003c\/strong\u003eEffects of Particle Sizes on DC -Biased Property of Fe-Si Alloy Atomized Powder Cores and Modeling\u003c\/p\u003e\u003cp\u003e\u003cstrong\u003e著者名: \u003c\/strong\u003e繁田 進(タムラ製作所),大島 泰雄(タムラ製作所),赤岩 功太(タムラ製作所)\u003c\/p\u003e\u003cp\u003e\u003cstrong\u003e著者名(英語): \u003c\/strong\u003eHanda Susumu(Tamura corporation),Oshima Yasuo(Tamura corporation),Akaiwa Kouta(Tamura corporation)\u003c\/p\u003e\u003cp\u003e\u003cstrong\u003eキーワード: \u003c\/strong\u003e圧粉磁心|透磁率|直流重畳特性|初磁化曲線|シミュレーション|ギャップ|powder core|permeability|DC-biased property| initial magnetization curve|simulation|gap\u003c\/p\u003e\u003cp\u003e\u003cstrong\u003e要約(日本語): \u003c\/strong\u003eFe－3.0mass%Si、Fe－6.5mass%Si合金ガスアトマイズ粉末を用いた圧粉磁心の直流重畳特性に及ぼす粉末粒子径の影響を検討した．これらの粉末を分級しないもの，63μm以上，63から53μm(63－53μmと略記する)，53－45μm， 45－38μm， 38－25μm ，25μm以下に分級して（Fe－3.0mass%Si、Fe－6.5mass%Si合金組成をそれぞれグループＡ，Ｂとする）7種類の粉末にわけ圧粉磁心を作製し直流重畳特性を評価した．また，ＮＭＧＢモデルを用いて直流重畳特性を計算し実測値との誤差を検討し，その結果に基づき粒子間隙分布を推定した．グループＡについて，分級した粒子径が小さくなる程，低磁界でのμdifが大きく，5k A\/mまでにおける一定領域が大きくなった．グループBについて，分級した粒子径が小さくなる程，低磁界でのμdifが小さく，5k A\/mまでにおける一定領域が大きくなった．つまり，両グループとも粒子径が小さくなる程直流重畳特性が良くなることがわかった．各グループの試料について，NMGBモデルを用い直流重畳特性を計算し実測値と比較した．グループＡ，Ｂ各7種類の試料で，磁界1.0～16 k A\/mの範囲において微分透磁率の実測値と計算値の相対誤差は，前者では25μm以下を除いて±3.9%以下，25μm以下では－6.7%，+4.8%，後者では63μm以上を除いて±3.3%以下，63μm以上では－4.0%，+5.6%となった．粒子間隙について，両グループとも粒子径が小さくなる程，幾何平均値は小さくなり幾何標準偏差値も小さくなった．\u003c\/p\u003e\u003cp\u003e\u003cstrong\u003e要約(英語): \u003c\/strong\u003eDC－biased magnetic properties of powder cores made of Fe－3.0mass%Si (Group A) and Fe－6.5mass%Si (Group B) alloy powders have been investigated using a nonmagnetic grain boundary (NMGB) model taking into account the distribution of gap width between particles.  These powders were sieved into upper 63μm，under 63μm and upper 53μm (named 63－53μm)，53－45μm， 45－38μm， 38－25μm ，under 25μm and no sieved one. B－H loops were measured, and differential permeability (μdif ) was calculated at each magnetic field. They were compared with the value calculated from the NMGB model taking into account the gap width distribution. The smaller the particle sizes were, the higher the μdif s were at low magnetic field for the group A and the smaller the particle sizes were, the smaller the μdif s were at low magnetic field for the group B. The smaller the powder size was, the better DC－biased properties were for the both groups. The calculated DC－biased properties by the NMGB model were compared with measured one. The relative inaccuracy from 1.0 to 16.0 kA\/m of the magnetic field was within ± 3.9 % except for under 25 μm and －6.7%，+4.8% for under 25 μm for the group A. The relative inaccuracy from 1.0 to 16.0 kA\/m of the magnetic field was within ± 3.3 % except for upper 63 μm and －4.0%，+5.6% for upper 63 μm for the group B. The gap width distributions were calculated by using the NMGB model. The smaller the particle sizes were, the smaller the geometric average particle sizes and standard deviations of the gaps were for the both groups.\u003c\/p\u003e\u003cp\u003e\u003cstrong\u003e原稿種別: \u003c\/strong\u003e日本語\u003c\/p\u003e\u003cp\u003e\u003cstrong\u003ePDFファイルサイズ: \u003c\/strong\u003e1,427 Kバイト\u003c\/p\u003e","brand":"IEEJ-PDF","offers":[{"title":"PDFダウンロード（一般価格330円\/会員価格220円） \/ A4 \/ 6","offer_id":46380685951215,"sku":"IEEJ-MAG11117-PDF","price":330.0,"currency_code":"JPY","in_stock":true}],"thumbnail_url":"\/\/cdn.shopify.com\/s\/files\/1\/0718\/9512\/2159\/files\/IEEJ-PDF_87292c9d-c715-416b-a044-bd6a4d572857.png?v=1744203395","url":"https:\/\/ieej.bookpark.ne.jp\/products\/ieej-mag11117","provider":"電気学会 電子図書館","version":"1.0","type":"link"}